Dry Sliding Wear Behaviour Of Heat Treated (t6) Aluminum Composite DE
-
- Englisch ausgewählt
38,99 €
UVP
45,20 €
inkl. gesetzl. MwSt.,
Beschreibung
Produktdetails
Einband
Taschenbuch
Erscheinungsdatum
06.06.2024
Verlag
LAP LAMBERT Academic PublishingSeitenzahl
52
Maße (L/B/H)
22/15/0,4 cm
Gewicht
96 g
Sprache
Englisch
ISBN
978-620-7-65206-8
In this study, Al6061 was reinforced with equal (4-16 wt. %) percentages ofSiC/MoS2 particles through stir casting technique. The cast samples were subjected toT6 Heat treatment. Artificial ageing treatment was carried out for a different du-ration (4-12 hours) with constant temperature of (155 o C). Wear tests was carried out by using pin on disc apparatus based on Taguchi's design, considering aging time, % reinforcement, speed, distance and load as input parameters. The concept of this project is to reduce the wear rate. The compositions of materials to be tested by using stir casting method to select the material combination for minimize the wear.Metal matrix composites (MMC) focuses primarily on improved specific strength, high temperature and wear resistance application. Aluminium matrix reinforced with Sic and MoS 2 in this project.Dry sliding wear behavior (AMC) analyzed with thehelp of pin on disc apparatus.
Noch keine Bewertungen vorhanden
Verfassen Sie die erste Bewertung zu diesem Artikel
Helfen Sie anderen Kundinnen und Kunden durch Ihre Meinung.
Kurze Frage zu unserer Seite
Vielen Dank für Ihr Feedback
Wir nutzen Ihr Feedback, um unsere Produktseiten zu verbessern. Bitte haben Sie Verständnis, dass wir Ihnen keine Rückmeldung geben können. Falls Sie Kontakt mit uns aufnehmen möchten, können Sie sich aber gerne an unseren Kund*innenservice wenden.
zum Kundenservice