Silica-supported iron catalysts were prepared using
an advanced non-aqueous evaporative deposition
technique, which leads to a catalyst with high
extents of reduction, high CO conversions, and high
C2+ hydrocarbons productivities. The catalysts were
tested following an L18 orthogonal array statistical
design approach. Primary independent variables
affecting catalysts activity were promoter type,
pretreatment gas composition, pretreatment and
reaction temperature. Steady state catalytic
activity is positively correlated with increasing
bulk chi-carbide content for silica-supported Fe and
FePt catalysts but not for FePtK.
The bulk and surface carbonaceous species was both
measured with high pressure in situ Mössbauer
spectroscopy and TPSR-MS. A correlation between the
amount of reactive -carbon (C ) and initial
catalytic activity was established. An modified
method was proposed for quantitative measurement of
irreversible CO site density on the iron catalysts.
Finally, a comprehensive model was proposed for iron
phase transformations during pretreatment, FTS and
post-reaction passivation/oxidation.
an advanced non-aqueous evaporative deposition
technique, which leads to a catalyst with high
extents of reduction, high CO conversions, and high
C2+ hydrocarbons productivities. The catalysts were
tested following an L18 orthogonal array statistical
design approach. Primary independent variables
affecting catalysts activity were promoter type,
pretreatment gas composition, pretreatment and
reaction temperature. Steady state catalytic
activity is positively correlated with increasing
bulk chi-carbide content for silica-supported Fe and
FePt catalysts but not for FePtK.
The bulk and surface carbonaceous species was both
measured with high pressure in situ Mössbauer
spectroscopy and TPSR-MS. A correlation between the
amount of reactive -carbon (C ) and initial
catalytic activity was established. An modified
method was proposed for quantitative measurement of
irreversible CO site density on the iron catalysts.
Finally, a comprehensive model was proposed for iron
phase transformations during pretreatment, FTS and
post-reaction passivation/oxidation.
Noch keine Bewertungen vorhanden
Verfassen Sie die erste Bewertung zu diesem Artikel
Helfen Sie anderen Kundinnen und Kunden durch Ihre Meinung.
Kurze Frage zu unserer Seite
Vielen Dank für Ihr Feedback
Wir nutzen Ihr Feedback, um unsere Produktseiten zu verbessern. Bitte haben Sie Verständnis, dass wir Ihnen keine Rückmeldung geben können. Falls Sie Kontakt mit uns aufnehmen möchten, können Sie sich aber gerne an unseren Kund*innenservice wenden.
zum Kundenservice